How can the lack of fusion defects be prevented ?

By Decibel -
How can the lack of fusion defects be prevented ?

  • use a sufficiently wide joint preparation
  • select welding parameters (high current level, short arc length, not too high a welding speed) to promote penetration into the joint side wall without causing flooding
  • ensure the electrode/gun angle and manipulation technique will give adequate side wall fusion
  • use weaving and dwell to improve side wall fusion providing there are no heat input restrictions
  • if arc blow occurs, reposition the current return, use AC (in MMA [SMA] welding) or demagnetise the steel

Join For PCN Welding Inspector Level 2 Program for Knowing More on Welding Technology and It's Details

http://decibelnde.com/weldinginspector.php

Popular posts from this blog

What is the Plate Lamination Defect?

By Decibel -
Image
Plate lamination defect is one of the primary processing discontinuity that originates during hot or cold forming processes and is considered as a serious metal plate defect.  All the metals contain discontinuities at micro and macro levels. These discontinuities, when above the acceptance level, are termed as defects. The discontinuities in metal are classified according to the stage of manufacturing in which they initiate.  Plate lamination defect can be defined as flat and thin subsurface separations present inside metal plate, parallel to the surface of the plates. The sources of this defect are inherent discontinuities present in metal such as inclusion and porosity, which are flattened during the rolling process.  Carbon Steel Plate Lamination Defect & Reasons A carbon steel plate is produced by the process of hot or cold rolling a thick slab. During this process, carbon steel may pass through the rollers many times to achieve the desired thickness. Each pass results in
Read more

Comparison of the use of rutile and cellulosic electrodes Knowledge Sharing From Decibel.

By Decibel -
Image
Comparison of the use of rutile and cellulosic electrodes Types of electrodes and their compositions Many types of manual metal arc (MMA) electrodes are available on the market. Depending on the main constituent of their flux, they are grouped into three categories: cellulosic, rutile and basic. All electrodes consist of a cored wire (typically 2.5–6mm diameter) coated by a flux. The core wire is generally made of low-quality riming steel and the fluxes contain many elements allowing refinement of the weld macrostructure. The composition of the flux impacts the electrodes’ behaviour. The main constituents of the different types of electrodes and the shielding gas created for each are described in Table 1 (Bowniszewski, 1979). Table 1 Main constituent of the three possible types of electrodes and shielding gas created by its combustion. Electrode type Main constituent Shielding gas created Rutile Titania (TiO2) Mainly CO2 Basic Calcium compounds Mainly CO2 Cellulosic
Read more

CSWIP Preparatory Classes in Kerala with 90 % Pass Rate.

By Decibel -
Image
Decibel Conducts CSWIP 3.1 Preparatory Courses in Kerala at Trivandrum and Pattambi Training Centers. Overall a 90% Pass rate yearly has been achieved regularly and Intensive Practicals for Understanding the concepts, familiarizing with the technology and crafting a welding inspector from RAW has been done always, by our expert faculty members. You may See the Qualified Faculties at our End for Understanding more on our Team. After Successful Completion of the Training & Examination you will be getting Free Placement Support for Enrich your career towards the next stage of your qualification. If you Fail in CSWIP 3.1 Exam we will provide Free of Cost Additional Training for you Till you Get Passed. Contact Decibel For More Details on 100% Pass for CSWIP 3.1
Read more